Luoyang Hongsheng Trading Co., Ltd

Quality Items

Unit

4.5

6

8

Reference

Thickness

μm

Standard-Strength

Medium-Strength

High-Strength

Standard-Strength

Medium-Strength

High-Strength

Ultra High-Strength

Standard-Strength

Medium-Strength

High-Strength

IPC-4562A

Area Weight

(g/m²)

40±2

54±2

72±2

IPC-TM-650 2.2.12.1

Tensile Strength
(Room Temperature)

Mpa

≥300

≥400

≥500

≥300

≥400

≥500

≥550

≥300

≥400

≥500

IPC-TM-650 2.4.18

Elongation
(Room Temperature)

%

≥3.0

≥2.0

≥2.0

≥5.0

≥3.0

≥2.0

≥2.0

≥7.0

≥5.0

≥3.0

Shiny Side/Drum Side Roughness(Ra)

μm

0.1-0.4

0.1-0.4

0.1-0.4

IPC-TM-650 2.2.17

Matte Side/Electrolyte Side Roughness(Rz)

μm

≤2.0

≤2.0

≤2.0

Purity

%

Cu≥99.9%

Cu≥99.9%

Cu≥99.9%

IPC-TM-650 2.3.15

Width Tolerance

mm

0, +2

0, +2

0, +2

Anit Oxidisation
(Heating at 140℃ for15 mins)

Non-Oxidation, Non-Discoloring

Tipical Applications

Used as a current collector for the anode of lithium batteries

Used as a current collector for the anode of lithium batteries

Used as a current collector for the anode of lithium batteries

Tipical Processes

Designed for cylindrical, prismatic and pouch cell types

1.Designed for cylindrical, prismatic and pouch cell types
2.High tensile properties will avoid deformation forcells with higher stacks
3.High tensile strength at room temperature allows the use of thinner foil and a load of more active material during the coating process(improved manufacturing yield).

1.Designed for cylindrical, prismatic and pouch cell types
2.High tensile properties will avoid deformation forcells with higher stacks
3.High tensile strength at room temperature allows the use of thinner foil and a load of more active material during the coating process(improved manufacturing yield).